Electron Beam Welding For Aluminum. Electron beam EB welding was performed on three different aluminium alloys namely alloys 2024 5005 and 6061 plate thickness 5 mm except alloy 5005 which was 3 mm in thickness to establish. Defect free welds were found in II specimen Fig.
This all adds up to make T2219 a very porosity prone alloy and basically difficult to weld properly. To test the sample geometry effect on the welding By using specimens 11 and 22 the hot cracking behavior of the electron beam welded AI-I050 to itself and AI-6061 to itself was determined. Beam welding techniques are commonly used for aluminum.
Electron Beam Welding Aluminum.
First the melted magnesium alloy with higher Al content has better fluidity to chink surface defects during electron beam welding but the γ phase Mg 17 AlZn 12 containing oxygen can be dissolved and form micropores during high energy electron beam welding. The paper deals with the analysis of mechanical properties of welded joints made of AW 2099 aluminium-lithium alloy by electron beam welding. At that different casting quality scenarios are set with the aid of the die casting process and the robustness of the joining method is investigated with. To test the sample geometry effect on the welding By using specimens 11 and 22 the hot cracking behavior of the electron beam welded AI-I050 to itself and AI-6061 to itself was determined.